AISI 6150
TYPICAL ANALYSIS
C.
0.50%
Mn.
0.75%
Cr.
1.00%
V.
0.15%
AISI 6150 is an oil quenching spring steel which offers good wear resistance after heat treatment.
Forging:
Forge AISI 6150 at 1050掳C. Do not work this steel when it has fallen below 840掳C.
Annealing:
Slow furnace cool from 840掳/860掳C.
Hardening:
Pre heat slowly to 650/700掳C and thoroughly soak the AISI 6150 component. Continue heating to the final hardening temperature of 850/870掳C and allow the AISI 6150 component to be heated through. Quench in oil.
Tempering:
Temper immediately after quenching whilst tools are still hand warm. Re-heat to the tempering temperature, soak for one hour per 25 millimetre of total thickness, 2 hours minimum, then cool in air. For most applications tempering of AISI 6150 will be between 400掳/600掳C.
Tempering 掳C
100
200
300
400
450
500
550
600
HRc
56
53
50
49
46
44
40
36
|
| |
|
|
|
 |
|
Xi'an Jiate Titanium Industry Co.,Ltd |
| |
Contact
Person: |
Alisa Zhang |
Phone: |
0086-29-85277651 |
Fax: |
0086-29-85490661 |
Zip code: |
710061 |
Address: |
NO.375 Changan South Road,Xian,Xian,Shaanxi |
| |
Web Site: |
http://www.cntitanium.com |
E-mail: |
alisa@jttitanium.com |
| |
|
|
 |
|
|